HMLS polyester tyre cord fabric
TEST ITEM | UNIT | 1000D/2 | 1300D/2 | 1500D/2 | 2000D/2 | 1300D/3 | 1500D/3 | 2000D/3 | |
BREAKING STRENGTH | N | ≥137 | ≥180 | ≥202 | ≥270 | ≥260 | ≥305 | ≥400 | |
ELONGATION AT SPECIFIC LOAD | 44.1N | % | 4.5±1.0 |
|
|
|
|
|
|
58.0N |
| 4.5±1.0 |
|
|
|
|
| ||
66.6N |
|
| 4.5±1.0 |
|
|
|
| ||
88.2N |
|
|
| 4.5±1.0 | 4.5±1.0 |
|
| ||
100N |
|
|
|
|
| 5.0±1.0 |
| ||
133N |
|
|
|
|
|
| 5.5±1.0 | ||
ELONGATION AT BREAK | % | ≥14 | ≥14 | ≥14 | ≥14 | ≥14 | ≥15 | ≥16 | |
H-ADHENSION 138℃*50min | N/10mm | ≥125 | ≥130 | ≥140 | ≥170 | ≥170 | ≥185 | ≥190 | |
DIP PICK UP | % | 3.5±1.0 | 3.0±1.0 | 3.0±1.0 | 3.0±1.0 | 3.0±1.0 | 3.0±1.0 | 2.5±1.0 | |
GAUGE | mm | 0.56±0.03 | 0.61±0.03 | 0.66±0.03 | 0.75±0.03 | 0.75±0.03 | 0.81±0.03 | 0.90±0.03 | |
PLY TEIST（S） | T/m | 450±15 | 390±15 | 370±15 | 330±15 | 330±15 | 300±15 | 260±15 | |
HOT AIR SHRINKAGE 177℃*2min*0.05CN/dtex | % | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | |
MOISTURE CONTENT | % | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | |
FABRIC WIDTH | cm | 145±3 | 145±3 | 145±3 | 145±3 | 145±3 | 145±3 | 140±2 | |